| PROPERTY | TEST METHOD | TYPE |
| Gauge, nominal (mils) | | 45 |
| Plies, reinforcing | | 10 x 10 |
| Denier | | 1000 |
Thickness, minimum (mils)
1. Overall
2. Over Scrim | ASTM D-751
Optical Method |
41
11 |
| Breaking Strength, fabric
minimum (lbs)
| ASTM D-751, Method A | 250 |
| Elongation at break - percentage | | 22 |
Low temperature
flexibility (EF) | ASTM D2136, 1/8 in. mandrel
4 hrs - Pass | -40 |
| Puncture resistance(lbs) | FTMS 101EC
Method 2031
| 210 |
Tear Strength
minimum (lbs | ASTM D-751, Method B
Tongue Tear | 55 |
Dimensional Stability
(percentage change, maximum) | ASTM D1204
180EF/1 hour | 1.0 |
Hydrostatic Resistance,
minimum (lbs) | ASTM 3751, Method A, Procedure 1 | 350 |
| Ply adhesion, minimum (lbs/in) | ASTM D-413, Machine Method | 20 |
Water Absorption
(maximum, % weight change) | ASTM D471 70EF | <1% |
| UV Resistance | a. Florida exposure
b. ASTM G26 Xenon arc method
63EC | pass 1 yr exposure
pass 3,000 hours |
Stress Cracking Resistance
(min hours with no failure) | ASTM D1693 | pass 3,000 hours |
SEAM PROPERTIES: |
| Bonded Seam Strength (lbs/width) | ASTM D-751, as modified in Appendix A NSF54 | 200 |
| Peel Adhesion, minimum (lbs/inch) | ASTM D413, as modified in Appendix A NSF54 | 20 |
| | |